1. Quality Stanrdard: Q/SHD004-2007 Item Type 75HD. Methoxy content (WT%) 19.0-24.0 Hydroxypropoxy conten (WT%) 4.0-12.0 Gelation temperature 70.0-90.0 Drying loss (WT%) ≤5.0 Residue on ignition (WT%) ≤1.0 pH (1% solution, 25) 4.0-8.0
2. Viscosity: (2% solution)
NDJ-1 B type Viscosimeter Rating Viscosity(mPa.s) Range Rating Viscosity(mPa.s) Range 4000 3600-4800
3. Hydroxypropyl Methylcellulose type indication:
2. Properties: 1. Appearance: white or similar to white granular powder; odorless 2. Properties: almost insoluble in ethanol, ether and acetone; quickly dispersed in 80-90 water; aqueous solution is very stable in room temperature; has good wetting/dispersing/adheisve/thickening/emlusifying/water preserving/film-forming properties; can prevent the infilration of grease; film formed has excellent flexibility and trransparency; has good compatibility with other emulsifier; easy salting-out. its solution is stable with PH 212. 3. Apparent density: 0.300.70g/cm3, densisty: 1.3g/cm3. 3. Dissolving process: HPMC will agglomerate when directly added to water and then dissolve. In this way it dissolves very slow and hard. Suggested methods as followers: 1. In hot water HPMC does not dissolve in hot water. The primary HPMC can be uniformly disperse in hot water. Then cool down in two ways: a) Add hot water in container and heated to over 70. Add HPMC gradually while slowly, stir. At the beginning, HPMC float on the top of water, then turns into slurry state stir and cool down. b) Add water in container to 1/3 or 2/3 of its content. Heated to over 70 add HPMC by sequence of a). Make it disperse to form slurry state. Add cool water or ice to the resideual content, stir and cool down the mixture.
4. Application It is widel used as thickener, adhesive, water preserving agent, film-forming agent in construction, building materials, dispersion coating, wallpaper paste, polymerization aids, leathers, printing ink and paper making etc.l also used in petroleum drilling and daily-use chemicals.